SIS SS-ISO 75-1988
塑料和硬橡胶．负载挠度的温度测定

Plastics and ebonite — Determination of temperature of deflection under load

SIS SS-ISO 75-1988 发布历史

1.1 This International Standard specifies two methods for the determination of the temperature of deflection under load (bending stress) of plastics and ebonite: — Method A, using a nominal surface stress of 1,80 MPa; — Method B, using a nominal surface stress of 0,45 MPa. 1.2 The methods specified are only applicable to materials that are rigid at room temperature, and are suitable for assess-ing the behaviour of plastics and ebonite at elevated temperature under load at a specified r?te of temperature in-crease. The results obtained do not necessarily represent maximum use temperatures, because in practice essential factors such as time, loading conditions and nominal surface stress may differ from the testing conditions. 1.3 The methods are more reproducible with amorphous plastics than with semi-crystalline ones and are not recom-mended for testing laminates. With some materials, it may be necessary to anneal the test specimens to obtain reliable results.

SIS SS-ISO 75-1988由SE-SIS 发布于 1988-11-15。

SIS SS-ISO 75-1988的历代版本如下：

• 1988年11月15日 SIS SS-ISO 75-1988 塑料和硬橡胶．负载挠度的温度测定

非常抱歉，我们暂时无法提供预览，您可以试试： 免费下载 SIS SS-ISO 75-1988 前三页，或者稍后再访问。

注意： 点击下载后，生成下载文件时间比较长，请耐心等待......

标准号

SIS SS-ISO 75-1988

发布日期

1988年11月15日

实施日期

废止日期

无

发布单位

SE-SIS

适用范围

1.1 This International Standard specifies two methods for the determination of the temperature of deflection under load (bending stress) of plastics and ebonite: — Method A, using a nominal surface stress of 1,80 MPa; — Method B, using a nominal surface stress of 0,45 MPa. 1.2 The methods specified are only applicable to materials that are rigid at room temperature, and are suitable for assess-ing the behaviour of plastics and ebonite at elevated temperature under load at a specified r?te of temperature in-crease. The results obtained do not necessarily represent maximum use temperatures, because in practice essential factors such as time, loading conditions and nominal surface stress may differ from the testing conditions. 1.3 The methods are more reproducible with amorphous plastics than with semi-crystalline ones and are not recom-mended for testing laminates. With some materials, it may be necessary to anneal the test specimens to obtain reliable results.