IEC 61788-2-1999
超导体 第2部分:临界电流测量 铌(3号)/锡复合超导体的临界直流电流

Superconductivity - Part 2: Critical current measurement - DC critical current of Nb₃Sn composite superconductors

IEC 61788-2-1999 发布历史

This part of IEC 61788 covers a test method for the determination of the d.c. critical current of Nb3Sn composite superconductors which are fabricated by either the bronze process or the internal tin diffusion process and have a copper/non-copper ratio larger than 0,2. This method is intended for use with superconductors which have critical currents of less than 1000 A and n-values larger than 12 under standard test conditions and at magnetic fields of less than or equal to 0,7 times the upper critical magnetic field. The test specimen is immersed in a liquid helium bath at a measured temperature during testing. The Nb3Sn composite test conductor has a monolithic structure with a total round-cross-sectional area that is less than 2 mm. The specimen geometry used in this test method is an inductively coiled specimen. Deviations from this test method that are allowed for routine tests and other specific restrictions are given in this standard. Nb3Sn conductors with critical currents above 1000 A or total cross-sectional areas greater than 2 mm can be measured with the present method with an anticipated reduction in precision and a more significant self-field effect (see annex C). Other, more specialized, specimen test geometries may be more appropriate for larger conductor testing which have been omitted from this present standard for simplicity and to retain precision. The test method given in this standard should in principle apply to Nb3Sn composite wires fabricated by any other process, such as the modified jelly-roll process. This method is also expected to apply to other superconducting composite wires after some appropriate modifications.

IEC 61788-2-1999由国际电工委员会 IX-IEC 发布于 1999-03。

IEC 61788-2-1999 在中国标准分类中归属于: L47 其他。

IEC 61788-2-1999的历代版本如下：

• 1999年03月 IEC 61788-2-1999 超导体 第2部分:临界电流测量 铌(3号)/锡复合超导体的临界直流电流
• 2006年11月 IEC 61788-2-2006 超导性.第2部分:临界电流测量.Nb<下标3>Sn复合超导体的直流临界电流

非常抱歉，我们暂时无法提供预览，您可以试试： 免费下载 IEC 61788-2-1999 前三页，或者稍后再访问。

注意： 点击下载后，生成下载文件时间比较长，请耐心等待......

标准号

IEC 61788-2-1999

发布日期

1999年03月

实施日期

废止日期

无

中国标准分类号

L47

发布单位

IX-IEC

代替标准

IEC 61788-2-2006

适用范围

This part of IEC 61788 covers a test method for the determination of the d.c. critical current of Nb3Sn composite superconductors which are fabricated by either the bronze process or the internal tin diffusion process and have a copper/non-copper ratio larger than 0,2. This method is intended for use with superconductors which have critical currents of less than 1000 A and n-values larger than 12 under standard test conditions and at magnetic fields of less than or equal to 0,7 times the upper critical magnetic field. The test specimen is immersed in a liquid helium bath at a measured temperature during testing. The Nb3Sn composite test conductor has a monolithic structure with a total round-cross-sectional area that is less than 2 mm. The specimen geometry used in this test method is an inductively coiled specimen. Deviations from this test method that are allowed for routine tests and other specific restrictions are given in this standard. Nb3Sn conductors with critical currents above 1000 A or total cross-sectional areas greater than 2 mm can be measured with the present method with an anticipated reduction in precision and a more significant self-field effect (see annex C). Other, more specialized, specimen test geometries may be more appropriate for larger conductor testing which have been omitted from this present standard for simplicity and to retain precision. The test method given in this standard should in principle apply to Nb3Sn composite wires fabricated by any other process, such as the modified jelly-roll process. This method is also expected to apply to other superconducting composite wires after some appropriate modifications.